When the glass is exposed to UV light with wavelengths between 280–320 nm, a
latent image is formed. The glass remains transparent at this stage, but its ability to absorb UV light increases. This increased absorption is only detectable using UV transmission spectroscopy and is caused by an
oxidation reduction reaction that occurs inside the glass during exposure. This reaction causes cerium ions to oxidize to a more stable state, and silver ions are reduced to silver.[5]
Post-exposure heat treatment
The latent image captured in the glass is made visible by heating.[6][2][4] This heat treatment is done by raising the temperature to about 500 °C to allow the oxidation-reduction reaction to form silver nanoclusters. Following this, the temperature is raised to 550–560 °C and
lithium metasilicate (Li2SiO3) forms on the silver nanoclusters. This material forms in the crystalline phase.[6]
HF chemical etching
The lithium metasilicate in the exposed regions of the glass can be etched by
hydrofluoric acid (HF). This forms glass microstructures with a roughness in the range of 5 μm, resulting in a three-dimensional image of the mask to be produced.[1] to 0.7 μm.[6]